A solution, quenching and ageing heat treatment is often performed on additive manufactured AlSi10Mg parts to dissolve the anisotropy due to the layer-by-layer building. This study investigates the influence of temperature and duration of solution and ageing treatment on microstructure, hardness and density of AlSi10Mg alloy produced by direct metal laser sintering. A parallel investigation is carried out on AlSi10Mg samples produced by gravity casting to analyse the different response to the same heat treatment conditions. The highest hardness, combined with an acceptable increase of porosity, is reached after selected heat treatment parameters. It was also found that, compared to the as-produced condition, this treatment leads to a decrease of ultimate tensile strength, without affecting the yield strength of additive manufactured samples, and reduces the difference in properties along the two building directions. The high properties of the as-produced samples are related to the finer microstructure and, as proved by the differential scanning calorimetric measurements, to the self-quenching phenomenon.
Study of heat treatment parameters for additively manufactured AlSi10Mg in comparison with corresponding cast alloy
Luca Girelli;Marialaura Tocci;Marcello Gelfi;Annalisa Pola
2019-01-01
Abstract
A solution, quenching and ageing heat treatment is often performed on additive manufactured AlSi10Mg parts to dissolve the anisotropy due to the layer-by-layer building. This study investigates the influence of temperature and duration of solution and ageing treatment on microstructure, hardness and density of AlSi10Mg alloy produced by direct metal laser sintering. A parallel investigation is carried out on AlSi10Mg samples produced by gravity casting to analyse the different response to the same heat treatment conditions. The highest hardness, combined with an acceptable increase of porosity, is reached after selected heat treatment parameters. It was also found that, compared to the as-produced condition, this treatment leads to a decrease of ultimate tensile strength, without affecting the yield strength of additive manufactured samples, and reduces the difference in properties along the two building directions. The high properties of the as-produced samples are related to the finer microstructure and, as proved by the differential scanning calorimetric measurements, to the self-quenching phenomenon.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.