We demonstrate room-temperature ferromagnetism in germanium counter-doped with manganese and arsenic at concentrations up to approximately 2.1 x 10(20) at/cm(3): these values are one order of magnitude lower than those at which ferromagnetic behavior has previously been observed. Synthesis proceeded by ion implantation at 513 K followed by annealing in argon at 673 K. High resolution TEM, STEM, and EDX show single-phase diamond cubic material lacking Mn or As precipitates. These findings are consistent with the prediction of Chen et al. that counter-doping with approximately equal concentrations of a single-electron donor permits Mn, a two-electron acceptor, to be incorporated at high enough concentrations to yield a diluted magnetic semiconductor with a Curie temperature above room temperature.
Room temperature ferromagnetism in low dose ion implanted counter-doped Ge:Mn, As
Donarelli, M.
;
2017-01-01
Abstract
We demonstrate room-temperature ferromagnetism in germanium counter-doped with manganese and arsenic at concentrations up to approximately 2.1 x 10(20) at/cm(3): these values are one order of magnitude lower than those at which ferromagnetic behavior has previously been observed. Synthesis proceeded by ion implantation at 513 K followed by annealing in argon at 673 K. High resolution TEM, STEM, and EDX show single-phase diamond cubic material lacking Mn or As precipitates. These findings are consistent with the prediction of Chen et al. that counter-doping with approximately equal concentrations of a single-electron donor permits Mn, a two-electron acceptor, to be incorporated at high enough concentrations to yield a diluted magnetic semiconductor with a Curie temperature above room temperature.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.