In this paper, we report the results about the synthesis and characterization of optimally doped La0.85Na0.15MnO 3 thin films deposited onto SrTiO3 (100), NdGaO 3 (100) and NdGaO3 (110) for thickness ranging from 11 to 82 nm. The effect of the substrate nature and orientation and film thickness was investigated in order to optimize the physical properties of the films. We obtained very smooth films displaying magnetoresistance values greater than 70% for temperature near to room temperature which makes them appealing for applicative purposes
Thin films of sodium-doped lanthanum manganites: role of substrate and thickness on the magnetoresistive response
ALESSANDRI, Ivano;
2004-01-01
Abstract
In this paper, we report the results about the synthesis and characterization of optimally doped La0.85Na0.15MnO 3 thin films deposited onto SrTiO3 (100), NdGaO 3 (100) and NdGaO3 (110) for thickness ranging from 11 to 82 nm. The effect of the substrate nature and orientation and film thickness was investigated in order to optimize the physical properties of the films. We obtained very smooth films displaying magnetoresistance values greater than 70% for temperature near to room temperature which makes them appealing for applicative purposesFile in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.