A concentration of Manganese as high as 8% was successfully diluted into Zinc Oxide epitaxial films deposited by pulsed laser deposition. The films showed strong ferromagnetism with a large coercivity. Low temperature X-ray absorption spectroscopy measurements indicated that all the Manganese ions substitute for Zinc sites of the wurtzite lattice in the valency of þ2. Photoluminescence measurements excluded the presence of Zinc vacancies, as well as Zn interstitials. All the magnetic moments measured were to ascribe to the formation of bound magnetic polarons, with no other contribution due to Manganese-secondary phases or Zinc vacancy-mediated double exchange interaction.
Chemical states and ferromagnetism in heavily Mn-substituted zinc oxide thin films.
CIPRIAN, Roberta;
2014-01-01
Abstract
A concentration of Manganese as high as 8% was successfully diluted into Zinc Oxide epitaxial films deposited by pulsed laser deposition. The films showed strong ferromagnetism with a large coercivity. Low temperature X-ray absorption spectroscopy measurements indicated that all the Manganese ions substitute for Zinc sites of the wurtzite lattice in the valency of þ2. Photoluminescence measurements excluded the presence of Zinc vacancies, as well as Zn interstitials. All the magnetic moments measured were to ascribe to the formation of bound magnetic polarons, with no other contribution due to Manganese-secondary phases or Zinc vacancy-mediated double exchange interaction.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.