On the determination of the point of fracture initiation by the load separation criterion in J-testing of ductile polymers

The application of an experimental approach based on the load separation criterion for the determination of the point of fracture initiation in a fracture test on a ductile polymer was critically examined. To this aim, the fracture process outlined by the application of this method was related to that described by the visual analysis of the fracture surfaces obtained in fracture tests on nominally identical specimens, in which different levels of crack extension were produced. The material examined was an acrylonitrile-butadiene-styrene (ABS) resin, and the fracture tests were performed at low loading rate on single-edge notched in bending specimens. The results demonstrated that this load separation criterion based methodology is a promising approach for the determination of the point of fracture initiation, and for material fracture resistance, JIc, evaluation. The method also has experimental simplicity and a high degree of repeatability.