In this paper, wear properties of samples manufactured using thixocasting were compared with those of components obtained using low-pressure die-casting and additive manufacturing in order to assess the relationship between material performance and production technologies, both conventional and innovative. The investigated items were made with AlSi7Mg alloy. First, microstructural analysis and hardness measurements were carried out. Subsequently, pin-on-disk wear tests were performed. Wear behavior of the samples was studied considering both coefficient of friction and wear rate, while the damage mechanism was analyzed by observation of the worn paths using scanning electron microscope, correlating the behavior to the specific microstructure. In addition, the effect of selected heat-treated conditions, relevant for real applications, on wear properties was also evaluated.
Properties of Semisolid Parts: Comparison with Conventional and Innovative Manufacturing Technologies
Tonolini, Pietro
;Pola, Annalisa;Montesano, Lorenzo;Tocci, Marialaura;Gelfi, Marcello;La Vecchia, Giovina Marina
2022-01-01
Abstract
In this paper, wear properties of samples manufactured using thixocasting were compared with those of components obtained using low-pressure die-casting and additive manufacturing in order to assess the relationship between material performance and production technologies, both conventional and innovative. The investigated items were made with AlSi7Mg alloy. First, microstructural analysis and hardness measurements were carried out. Subsequently, pin-on-disk wear tests were performed. Wear behavior of the samples was studied considering both coefficient of friction and wear rate, while the damage mechanism was analyzed by observation of the worn paths using scanning electron microscope, correlating the behavior to the specific microstructure. In addition, the effect of selected heat-treated conditions, relevant for real applications, on wear properties was also evaluated.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.