Additive manufacturing of Al alloys can represent an interesting solution for highperformance components in various industrial fields, as for instance the automotive and aerospace industry. Often, for these applications, the alloys are required to withstand exposure to high temperatures. Therefore, the investigation of the evolution of material properties with increasing temperature is of utmost importance in order to assess their suitability for this kind of applications. In the present study, tensile properties at high temperature were investigated for an AlSi10Mg alloy. Samples were manufactured by laser-based powder bed fusion in horizontal and vertical direction in order to examine the influence of building direction on material behavior. The samples were tested in as-built condition and after exposure to high temperature. Tensile tests were performed up to 150 °C and the effect of holding time at the test temperature was evaluated. Furthermore, the alloy was characterized by mechanical spectroscopy in order to evaluate the behavior of dynamic modulus with temperature and, thus, to provide a comprehensive characterization of the material behavior. It was found that the peculiar microstructure of the alloy produced by additive manufacturing is responsible for good high-temperature strength of the material up to 150 °C. The material also exhibits a good thermal stability even after holding at test temperature for 10 h.
Study of high temperature properties of AlSi10Mg alloy produced by laser-based powder bed fusion
Tocci M.;Pola A.
2021-01-01
Abstract
Additive manufacturing of Al alloys can represent an interesting solution for highperformance components in various industrial fields, as for instance the automotive and aerospace industry. Often, for these applications, the alloys are required to withstand exposure to high temperatures. Therefore, the investigation of the evolution of material properties with increasing temperature is of utmost importance in order to assess their suitability for this kind of applications. In the present study, tensile properties at high temperature were investigated for an AlSi10Mg alloy. Samples were manufactured by laser-based powder bed fusion in horizontal and vertical direction in order to examine the influence of building direction on material behavior. The samples were tested in as-built condition and after exposure to high temperature. Tensile tests were performed up to 150 °C and the effect of holding time at the test temperature was evaluated. Furthermore, the alloy was characterized by mechanical spectroscopy in order to evaluate the behavior of dynamic modulus with temperature and, thus, to provide a comprehensive characterization of the material behavior. It was found that the peculiar microstructure of the alloy produced by additive manufacturing is responsible for good high-temperature strength of the material up to 150 °C. The material also exhibits a good thermal stability even after holding at test temperature for 10 h.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.