nanoGraphite (nanoG) having a high surface area and a high shape anisotropy, defined as the ratio between the crystallite dimensions in a direction orthogonal and parallel to structural layers, was used to prepare nanocomposites based on poly(1,4-cis-isoprene) (IR), in the neat polymer matrix and in the presence of carbon black (CB). Tensile and dynamicmechanical measurements showed that nanoG forms a filler network at a relatively low concentration in neat IR and a hybrid filler network at a lower nanoG concentration in the presence of CB. A synergistic effect between the two carbon allotropes was found: composites containing both fillers present initial modulus values much higher than those calculated through the simple addition of the initial moduli of the composites containing only CB or nanoG.

Filler networking of a nanographite with a high shape anisotropy and synergism with carbon black in poly(1,4-cis-isoprene)-based nanocomposites

AGNELLI, Silvia;PANDINI, Stefano;
2014-01-01

Abstract

nanoGraphite (nanoG) having a high surface area and a high shape anisotropy, defined as the ratio between the crystallite dimensions in a direction orthogonal and parallel to structural layers, was used to prepare nanocomposites based on poly(1,4-cis-isoprene) (IR), in the neat polymer matrix and in the presence of carbon black (CB). Tensile and dynamicmechanical measurements showed that nanoG forms a filler network at a relatively low concentration in neat IR and a hybrid filler network at a lower nanoG concentration in the presence of CB. A synergistic effect between the two carbon allotropes was found: composites containing both fillers present initial modulus values much higher than those calculated through the simple addition of the initial moduli of the composites containing only CB or nanoG.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11379/409506
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 62
  • ???jsp.display-item.citation.isi??? 58
social impact